SPI Mold Finish – Practical Approach

Mold Finish – SPI Standard and the practical approach

SPI is the short form of the Society of Plastic Industry, who establish standards for plastic industry and the SPI Plastic Engineering Handbooks is one of the most important reference for engineers.

SPI defines the polishing standard on mold finish and widely applied in US markets. It helps to avoid grey areas and measure the finest of surface in the unit of Rough Average (Ra).

Nowadays, China’s standard is very much in line with SPI. However, there is little help using Ra value in China mold making industry because there is little chance to have precise equipment at site to do the precision measurement. What we needed is a practical guideline to more or less achieve the desired mold finish. Below guideline is widely accepted.

GLOSSY SURFACE, DIAMOND BUFF POLISH

SPI Finish A-1 — Grade #3, 6000 Grit Diamond Buff

SPI Finish A-2 — Grade #6, 3000 Grit Diamond Buff

SPI Finish A-3 — Grade #15, 1200 Grit Diamond Buff

NON-GLOSSY SURFACE, PAPER POLISH

SPI Finish B-1 — 600 Grit Paper

SPI Finish B-2 — 400 Grit Paper

SPI Finish B-3 — 320 Grit Paper

ROUGH SURFACE, STONE POLISH

SPI Finish C-1 — 600 Grit Stone

SPI Finish C-2 — 400 Grit Stone

SPI Finish C-3 — 320 Grit Stone

VERY ROUGH SURFACE, DRY BLASH POLISH

SPI Finish D-1 — 600 Stone Prior to Dry Blast Glass Bead #11

SPI Finish D-2 — 400 Stone Prior to Dry Blast #240 Oxide

SPI Finish D-3 — 320 Stone Prior to Dry Blast #24 Oxide

However, the above guideline falls short because it does not mention what steel should be used. For coarse surface, it may be fine. For demanding high glossy mold finish, the mold steel can be critical and the high glossy cannot be achieved without proper steel.  

For molding process, a melt plastic resin will be injected into a steel mold at high pressure and the steel will always face the issue of wear off. To produce a glossy product, the mold has to be significantly hard so that the shiny smooth surface will not be deteriorated quickly and the glossy surface can be remained for a longer period of time. The finer the surface is needed, the harder and the finer the steel is required.

Below is a supplementary guideline regarding steel to be used.

SPI Finish A1 – S136 Hardness at 54HRC

(Generally called “Super High Glossy” in China)

SPI Finish A2 – 718HH or NAK80 Hardness at 40HRC

(Generally called “High Glossy” in China)

SPI Finish A3 – 718H or S136 Hardness 32HRC

(Generally called “Normal Glossy” in China)

It is true that the steel made in China are somehow less consistent than from overseas. Therefore, it is suggested to use imported steel for demanding quality mold or at least use higher grade of steel from China to provide some buffer for the desired mold finish that you need.

Lastly, a high glossy mold finish is not equivalent to a high glossy finished product. It is significantly subject to other factors such as plastic resin used, molding condition and mold design. For example, ABS will provide higher glossy than PP, high temperature molding condition and non-flat surface will help to provide a much glossy finished product.

340 Responses to SPI Mold Finish – Practical Approach

  1. Sherwood Vintimilla says:

    Yet another good post.

  2. Yuk Meilleur says:

    nice post. You made some great points.

  3. Ward Mundell says:

    I just want to mention I am very new to blogging and site-building and seriously enjoyed your website. Probably I’m planning to bookmark your blog post . You really come with really good posts. Cheers for revealing your web page.

  4. Melissia Thorington says:

    Excellent stuff. I am unable to describe just how much your website has solved the problem within my academic research about them. I am now going to get top marks for certain. Thanks millions of. I owe you one.

  5. Lily says:

    Hi there, I found your blog by means of Google even as searching for a comparable matter, your website came up, it looks great. I have bookmarked to my favourites|added to my bookmarks.

  6. Mirta Soldavini says:

    I do consider all of the ideas you have presented for your post. They’re really convincing and will certainly work. Nonetheless, the posts are too quick for beginners. May you please lengthen them a bit from subsequent time? Thank you for the post.

  7. Gilbert Mattke says:

    Thanks for uploading this article and resources its really help full for my interests!! Gilbert Mattke

  8. Hai Vence says:

    This is my first time i visit here. I found so many entertaining stuff in your blog, especially its discussion. From the tons of comments on your articles, I guess I am not the only one having all the leisure here! Keep up the good work.

  9. Emanuel Sang says:

    Just saying thanks will not just be sufficient, for the tremendous lucidity in your writing. I will right away grab your rss feed to stay abreast of any updates.

  10. Karmen Goerlitz says:

    Excellent beat ! I wish to apprentice while you amend your web site, how can i subscribe for a blog site? The account aided me a acceptable deal. I had been a little bit acquainted of this your broadcast provided bright clear idea

Leave a Reply

Your email address will not be published. Required fields are marked *