SPI Mold Finish – Practical Approach

Mold Finish – SPI Standard and the practical approach

SPI is the short form of the Society of Plastic Industry, who establish standards for plastic industry and the SPI Plastic Engineering Handbooks is one of the most important reference for engineers.

SPI defines the polishing standard on mold finish and widely applied in US markets. It helps to avoid grey areas and measure the finest of surface in the unit of Rough Average (Ra).

Nowadays, China’s standard is very much in line with SPI. However, there is little help using Ra value in China mold making industry because there is little chance to have precise equipment at site to do the precision measurement. What we needed is a practical guideline to more or less achieve the desired mold finish. Below guideline is widely accepted.

GLOSSY SURFACE, DIAMOND BUFF POLISH

SPI Finish A-1 — Grade #3, 6000 Grit Diamond Buff

SPI Finish A-2 — Grade #6, 3000 Grit Diamond Buff

SPI Finish A-3 — Grade #15, 1200 Grit Diamond Buff

NON-GLOSSY SURFACE, PAPER POLISH

SPI Finish B-1 — 600 Grit Paper

SPI Finish B-2 — 400 Grit Paper

SPI Finish B-3 — 320 Grit Paper

ROUGH SURFACE, STONE POLISH

SPI Finish C-1 — 600 Grit Stone

SPI Finish C-2 — 400 Grit Stone

SPI Finish C-3 — 320 Grit Stone

VERY ROUGH SURFACE, DRY BLASH POLISH

SPI Finish D-1 — 600 Stone Prior to Dry Blast Glass Bead #11

SPI Finish D-2 — 400 Stone Prior to Dry Blast #240 Oxide

SPI Finish D-3 — 320 Stone Prior to Dry Blast #24 Oxide

However, the above guideline falls short because it does not mention what steel should be used. For coarse surface, it may be fine. For demanding high glossy mold finish, the mold steel can be critical and the high glossy cannot be achieved without proper steel.  

For molding process, a melt plastic resin will be injected into a steel mold at high pressure and the steel will always face the issue of wear off. To produce a glossy product, the mold has to be significantly hard so that the shiny smooth surface will not be deteriorated quickly and the glossy surface can be remained for a longer period of time. The finer the surface is needed, the harder and the finer the steel is required.

Below is a supplementary guideline regarding steel to be used.

SPI Finish A1 – S136 Hardness at 54HRC

(Generally called “Super High Glossy” in China)

SPI Finish A2 – 718HH or NAK80 Hardness at 40HRC

(Generally called “High Glossy” in China)

SPI Finish A3 – 718H or S136 Hardness 32HRC

(Generally called “Normal Glossy” in China)

It is true that the steel made in China are somehow less consistent than from overseas. Therefore, it is suggested to use imported steel for demanding quality mold or at least use higher grade of steel from China to provide some buffer for the desired mold finish that you need.

Lastly, a high glossy mold finish is not equivalent to a high glossy finished product. It is significantly subject to other factors such as plastic resin used, molding condition and mold design. For example, ABS will provide higher glossy than PP, high temperature molding condition and non-flat surface will help to provide a much glossy finished product.

341 Responses

  1. Kina Malstrom says:

    Really impressed! Everything is very, very clear, open is a description of the problem. It contains the information.

  2. Faustino Cyrus says:

    Heya i am for the first time here. I found this board and I find It truly useful & it helped me out much. I hope to give something back and aid others like you aided me.

  3. Mozell Ferron says:

    You are a very clever individual!

  4. Don Bardney says:

    I really enjoyed this post. You explain this topic very well. I really love your blog and I will definetly bookmark it

  5. Johnny Rimson says:

    Wow! Thank you! I always needed to write on my site something like that. Can I take a fragment of your post to my blog?

  6. Arron Notter says:

    Thanks so much for giving everyone an extraordinarily brilliant opportunity to read in detail from this blog. It’s always very useful and also full of a great time for me and my office mates to visit your blog at minimum thrice in 7 days to study the fresh guidance you will have. And indeed, I am just usually happy with all the brilliant principles you serve. Certain two ideas on this page are unquestionably the most suitable I’ve ever had.

  7. Jackqueline Callo says:

    I’m still learning from you, as I’m making my way to the top as well. I absolutely liked reading all that is posted on your blog.Keep the articles coming. I enjoyed it!

  8. Natalya Euton says:

    I truly wanted to type a note in order to appreciate you for those lovely tips and hints you are giving at this website. My time consuming internet search has now been honored with reputable insight to talk about with my visitors. I ‘d suppose that most of us website visitors actually are very much blessed to dwell in a fabulous network with so many lovely people with very beneficial tricks. I feel very much lucky to have used your webpages and look forward to tons of more enjoyable minutes reading here. Thank you again for everything.

  9. Reginald Mcfarlane says:

    I’m still learning from you, as I’m improving myself. I absolutely love reading everything that is posted on your website.Keep the tips coming. I enjoyed it!

  10. Eliseo Albery says:

    Wonderful goods from you, man. I’ve understand your stuff previous to and you’re just extremely wonderful. I really like what you’ve acquired here, certainly like what you are stating and the way in which you say it. You make it entertaining and you still take care of to keep it wise. I can’t wait to read much more from you. This is really a wonderful site.

Leave a Reply

Your email address will not be published. Required fields are marked *