SPI Mold Finish – Practical Approach

Mold Finish – SPI Standard and the practical approach

SPI is the short form of the Society of Plastic Industry, who establish standards for plastic industry and the SPI Plastic Engineering Handbooks is one of the most important reference for engineers.

SPI defines the polishing standard on mold finish and widely applied in US markets. It helps to avoid grey areas and measure the finest of surface in the unit of Rough Average (Ra).

Nowadays, China’s standard is very much in line with SPI. However, there is little help using Ra value in China mold making industry because there is little chance to have precise equipment at site to do the precision measurement. What we needed is a practical guideline to more or less achieve the desired mold finish. Below guideline is widely accepted.

GLOSSY SURFACE, DIAMOND BUFF POLISH

SPI Finish A-1 — Grade #3, 6000 Grit Diamond Buff

SPI Finish A-2 — Grade #6, 3000 Grit Diamond Buff

SPI Finish A-3 — Grade #15, 1200 Grit Diamond Buff

NON-GLOSSY SURFACE, PAPER POLISH

SPI Finish B-1 — 600 Grit Paper

SPI Finish B-2 — 400 Grit Paper

SPI Finish B-3 — 320 Grit Paper

ROUGH SURFACE, STONE POLISH

SPI Finish C-1 — 600 Grit Stone

SPI Finish C-2 — 400 Grit Stone

SPI Finish C-3 — 320 Grit Stone

VERY ROUGH SURFACE, DRY BLASH POLISH

SPI Finish D-1 — 600 Stone Prior to Dry Blast Glass Bead #11

SPI Finish D-2 — 400 Stone Prior to Dry Blast #240 Oxide

SPI Finish D-3 — 320 Stone Prior to Dry Blast #24 Oxide

However, the above guideline falls short because it does not mention what steel should be used. For coarse surface, it may be fine. For demanding high glossy mold finish, the mold steel can be critical and the high glossy cannot be achieved without proper steel.  

For molding process, a melt plastic resin will be injected into a steel mold at high pressure and the steel will always face the issue of wear off. To produce a glossy product, the mold has to be significantly hard so that the shiny smooth surface will not be deteriorated quickly and the glossy surface can be remained for a longer period of time. The finer the surface is needed, the harder and the finer the steel is required.

Below is a supplementary guideline regarding steel to be used.

SPI Finish A1 – S136 Hardness at 54HRC

(Generally called “Super High Glossy” in China)

SPI Finish A2 – 718HH or NAK80 Hardness at 40HRC

(Generally called “High Glossy” in China)

SPI Finish A3 – 718H or S136 Hardness 32HRC

(Generally called “Normal Glossy” in China)

It is true that the steel made in China are somehow less consistent than from overseas. Therefore, it is suggested to use imported steel for demanding quality mold or at least use higher grade of steel from China to provide some buffer for the desired mold finish that you need.

Lastly, a high glossy mold finish is not equivalent to a high glossy finished product. It is significantly subject to other factors such as plastic resin used, molding condition and mold design. For example, ABS will provide higher glossy than PP, high temperature molding condition and non-flat surface will help to provide a much glossy finished product.

341 Responses

  1. Chris Liz says:

    Well I truly enjoyed studying it. This post offered by you is very effective for correct planning.

  2. Caron Jubb says:

    I have been checking out a few of your articles and i can claim pretty nice stuff. I will surely bookmark your site.

  3. Danial Cissell says:

    Heya i’m for the first time here. I found this board and I find It truly useful & it helped me out much.

  4. Dario Lent says:

    I don’t even know how I ended up here, but I thought this post was great. I do not know who you are but certainly you are going to a famous blogger if you aren’t already 😉 Cheers!

  5. Jamaal Portland says:

    Great blog! I am loving it!! Will be back later to read some more. I am taking your feeds also

  6. Celine Prater says:

    Fantastic goods from you, man. I’ve understand your stuff previous to and you’re just too great. I really like what you have acquired here, certainly like what you are stating and the way in which you say it. You make it entertaining and you still care for to keep it wise. I cant wait to read far more from you. This is actually a wonderful web site.

  7. Odelia Leason says:

    I like the helpful information you provide in your articles. I will bookmark your weblog and check again here regularly. I am quite sure I’ll learn plenty of new stuff right here! Best of luck for the next!

  8. Agueda Faske says:

    Thank you a lot for giving everyone an exceptionally nice chance to read articles and blog posts from this site. It is usually so good and also stuffed with amusement for me personally and my office friends to visit your website particularly three times a week to study the new tips you have. And lastly, we are certainly motivated for the good creative ideas you serve. Certain 3 tips in this post are completely the very best we have all ever had.

  9. Maurice Marro says:

    I am not sure where you are getting your info, but great topic. I needs to spend some time learning more or understanding more. Thanks for magnificent information I was looking for this info for my mission.

  10. Clay Feagans says:

    Hi there, You’ve done a fantastic job. I’ll certainly digg it and personally suggest to my friends. I’m confident they’ll be benefited from this web site.

Leave a Reply

Your email address will not be published. Required fields are marked *