SPI Mold Finish – Practical Approach

Mold Finish – SPI Standard and the practical approach

SPI is the short form of the Society of Plastic Industry, who establish standards for plastic industry and the SPI Plastic Engineering Handbooks is one of the most important reference for engineers.

SPI defines the polishing standard on mold finish and widely applied in US markets. It helps to avoid grey areas and measure the finest of surface in the unit of Rough Average (Ra).

Nowadays, China’s standard is very much in line with SPI. However, there is little help using Ra value in China mold making industry because there is little chance to have precise equipment at site to do the precision measurement. What we needed is a practical guideline to more or less achieve the desired mold finish. Below guideline is widely accepted.

GLOSSY SURFACE, DIAMOND BUFF POLISH

SPI Finish A-1 — Grade #3, 6000 Grit Diamond Buff

SPI Finish A-2 — Grade #6, 3000 Grit Diamond Buff

SPI Finish A-3 — Grade #15, 1200 Grit Diamond Buff

NON-GLOSSY SURFACE, PAPER POLISH

SPI Finish B-1 — 600 Grit Paper

SPI Finish B-2 — 400 Grit Paper

SPI Finish B-3 — 320 Grit Paper

ROUGH SURFACE, STONE POLISH

SPI Finish C-1 — 600 Grit Stone

SPI Finish C-2 — 400 Grit Stone

SPI Finish C-3 — 320 Grit Stone

VERY ROUGH SURFACE, DRY BLASH POLISH

SPI Finish D-1 — 600 Stone Prior to Dry Blast Glass Bead #11

SPI Finish D-2 — 400 Stone Prior to Dry Blast #240 Oxide

SPI Finish D-3 — 320 Stone Prior to Dry Blast #24 Oxide

However, the above guideline falls short because it does not mention what steel should be used. For coarse surface, it may be fine. For demanding high glossy mold finish, the mold steel can be critical and the high glossy cannot be achieved without proper steel.  

For molding process, a melt plastic resin will be injected into a steel mold at high pressure and the steel will always face the issue of wear off. To produce a glossy product, the mold has to be significantly hard so that the shiny smooth surface will not be deteriorated quickly and the glossy surface can be remained for a longer period of time. The finer the surface is needed, the harder and the finer the steel is required.

Below is a supplementary guideline regarding steel to be used.

SPI Finish A1 – S136 Hardness at 54HRC

(Generally called “Super High Glossy” in China)

SPI Finish A2 – 718HH or NAK80 Hardness at 40HRC

(Generally called “High Glossy” in China)

SPI Finish A3 – 718H or S136 Hardness 32HRC

(Generally called “Normal Glossy” in China)

It is true that the steel made in China are somehow less consistent than from overseas. Therefore, it is suggested to use imported steel for demanding quality mold or at least use higher grade of steel from China to provide some buffer for the desired mold finish that you need.

Lastly, a high glossy mold finish is not equivalent to a high glossy finished product. It is significantly subject to other factors such as plastic resin used, molding condition and mold design. For example, ABS will provide higher glossy than PP, high temperature molding condition and non-flat surface will help to provide a much glossy finished product.

340 Responses to SPI Mold Finish – Practical Approach

  1. Shelli Huenergardt says:

    Great blog! I am loving it!! Will come back again. I am bookmarking your feeds also

  2. Matthew Lessen says:

    I wanted to put you the little observation to finally say thanks once again just for the spectacular tips you’ve documented in this article. It has been really surprisingly open-handed with you to present without restraint precisely what a few people would’ve sold for an e book to get some cash on their own, most notably seeing that you might well have tried it if you ever decided. These creative ideas as well worked to become a good way to fully grasp that someone else have a similar dreams similar to my personal own to figure out more regarding this issue. Certainly there are numerous more pleasant situations in the future for individuals who check out your site.

  3. Trista Jandres says:

    Hello.This post was extremely fascinating, especially since I was searching for thoughts on this topic last couple of days.

  4. Fernanda Desroches says:

    It’s such a great site

  5. Neville Stevick says:

    Heya i am for the first time here. I found this board and I find It truly useful & it helped me out a lot. I hope to give something back and aid others like you aided me.

  6. Faustina Scally says:

    Super-Duper website! I am loving it!! Will come back again. I am taking your feeds also

  7. Burton Haynes says:

    I precisely wished to appreciate you yet again. I do not know the things I would have undertaken without the actual pointers discussed by you regarding this concern. It became the terrifying case for me, nevertheless discovering this specialized approach you treated it made me to cry for gladness. I’m just happy for your guidance as well as sincerely hope you really know what an amazing job you are accomplishing instructing the others all through your website. I’m certain you have never come across all of us.

  8. Phung Vanoy says:

    Thanks a lot for giving everyone an exceptionally superb possiblity to read critical reviews from this blog. It is often so fantastic and as well , full of amusement for me personally and my office mates to visit your blog really 3 times per week to study the latest guidance you have got. And of course, I am actually astounded concerning the striking suggestions you give. Certain 4 ideas in this post are really the most effective I have ever had.

  9. Marleen Mullis says:

    I simply desired to thank you so much yet again. I’m not certain what I would have followed without the type of methods provided by you over such a situation. This has been a very hard setting in my view, nevertheless taking note of a professional approach you managed that forced me to jump over joy. I’m just happy for this guidance and even hope you recognize what a powerful job that you are accomplishing educating many people by way of your blog post. Probably you have never met any of us.

  10. Cordelia Oltman says:

    Pretty nice post. I just stumbled upon your weblog and wanted to say that I have truly enjoyed surfing around your blog posts. After all I will be subscribing to your feed and I hope you write again very soon!

Leave a Reply

Your email address will not be published. Required fields are marked *